| Item | Index |
| The thickness(mm) | 0.5 | 0.75 | 1.00 | 1.25 | 1.5 | 2.00 | 2.25
| 3.00 |
| Tensile yield strength (longitudinal and transverse)N/mm | ≧8 | ≧11 | ≧15 | ≧18 | ≧22 | ≧29 | ≧37 | ≧44 |
| Tensile fracture strength (longitudinal and transverse)N/mm | ≧13 | ≧20 | ≧27 | ≧33 | ≧40 | ≧53 | ≧67 | ≧80 |
| Yield elongation (longitudinal and transverse)% | ≧12 |
| Elongation at break (longitudinal and transverse)% | ≧700 |
| Right-angle tearing load (longitudinal and transverse)N | ≧58 | ≧93 | ≧125 | ≧160 | ≧190 | ≧250 | ≧315 | ≧375 |
| Puncture resistance N | ≧160 | ≧240 | ≧320 | ≧400 | ≧480 | ≧640 | ≧800 | ≧960 |
| Stress cracking under tensile load (dead-load tensile method with notch)h | ≧300 |
| Carbon black content% | 2.0~3.0 |
| Oxidation induction time(OIT) | Induction time of oxidation at atmospheric pressure≧100 |
| Induction time of high pressure oxidation≧400 |
| 85℃ thermal aging (OIT retention rate at atmospheric pressure after 90 days) | ≧55 |
| Uv resistance (OIT retention rate after 1600h UV irradiation) | ≧50 |